- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.25
- 缺口冲击强度: 0.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 - 1.55 g/cc | 0.0524 - 0.0560 lb/in³ | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.670 - 0.750 g/cc | 0.0242 - 0.0271 lb/in³ | IS 867-1963 |
| Water Absorption | 0.25 - 0.50 % | 0.25 - 0.50 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | Compression specimen; IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 40.0 - 50.0 MPa | 5800 - 7250 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 66.0 - 75.0 MPa | 9570 - 10900 psi | IS 867-1963 |
| Izod Impact, Notched | 0.200 - 0.300 J/cm | 0.375 - 0.562 ft-lb/in | IS 13411-1992 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 - 3.16e+11 ohm-cm | 1.00e+11 - 3.16e+11 ohm-cm | IS 3396-1979 |
| Surface Resistance | 1.00e+10 - 1.00e+11 ohm | 1.00e+10 - 1.00e+11 ohm | IS 3396-1979 |
| Dielectric Strength | 5.50 - 7.50 kV/mm @Temperature 90.0 °C | 140 - 191 kV/in @Temperature 194 °F | IS 2584-1963 |
| Comparative Tracking Index | >= 125 V | >= 125 V | 2824-1975 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | >= 200 °C | >= 392 °F | 2 hours |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 65.0 - 85.0 °C | 149 - 185 °F | |
| Front Barrel Temperature | 85.0 - 95.0 °C | 185 - 203 °F | |
| Nozzle Temperature | <= 105 °C | <= 221 °F | |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Injection Pressure | 98.0 - 196 MPa | 14200 - 28400 psi | |
| Hold Pressure | 58.8 MPa | 8530 psi | |
| Cure Time | 0.333 - 0.500 min | 0.00556 - 0.00833 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |