- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.25
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 - 1.38 g/cc | 0.0488 - 0.0499 lb/in³ | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.620 - 0.700 g/cc | 0.0224 - 0.0253 lb/in³ | IS 867-1963 |
| Water Absorption | 0.30 - 0.50 % | 0.30 - 0.50 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0076 - 0.0086 cm/cm | 0.0076 - 0.0086 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | >= 46.0 MPa | >= 6670 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 60.0 - 70.0 MPa | 8700 - 10200 psi | IS 867-1963 |
| Izod Impact, Notched | >= 0.250 J/cm | >= 0.468 ft-lb/in | IS 13411-1992 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+10 - 3.16e+10 ohm-cm | 1.00e+10 - 3.16e+10 ohm-cm | IS 3396-1979 |
| Surface Resistance | 1.00e+9 - 3.16e+9 ohm | 1.00e+9 - 3.16e+9 ohm | IS 3396-1979 |
| Dielectric Strength | 3.00 - 5.00 kV/mm @Temperature 90.0 °C | 76.2 - 127 kV/in @Temperature 194 °F | IS 2584-1963 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Moisture Content | 4.0 - 5.5 % | 4.0 - 5.5 % | |
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
| Cure Time | 0.333 - 0.417 min | 0.00556 - 0.00694 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |