- 密度 [g/cm3]: 0.024
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0240 g/cc | 0.000868 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 0.345 MPa | >= 50.0 psi | Bare, min, preliminary value obtained from limited testing |
| >= 0.379 MPa | >= 55.0 psi | Stabilized, min, preliminary value obtained from limited testing | |
| >= 0.483 MPa | >= 70.0 psi | Bare, typ, preliminary value obtained from limited testing | |
| >= 0.552 MPa | >= 80.0 psi | Stabilized, typ, preliminary value obtained from limited testing | |
| Compressive Modulus | 0.0483 GPa | 7.00 ksi | Stabilized, typ, preliminary value obtained from limited testing |
| Shear Modulus | 0.0117 GPa | 1.70 ksi | Plate Shear, W Direction, typ, preliminary value obtained from limited testing |
| 0.0234 GPa | 3.40 ksi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing | |
| Shear Strength | >= 0.172 MPa | >= 25.0 psi | Plate Shear, W Direction, min, preliminary value obtained from limited testing |
| 0.241 MPa | 35.0 psi | Plate Shear, W Direction, typ, preliminary value obtained from limited testing | |
| >= 0.379 MPa | >= 55.0 psi | Plate Shear, L Direction, min, preliminary value obtained from limited testing | |
| 0.483 MPa | 70.0 psi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing | |