- 密度 [g/cm3]: 0.0641
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0641 g/cc | 0.00231 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 2.76 MPa | >= 400 psi | Bare, min |
| 3.31 MPa | 480 psi | Bare, typ | |
| >= 3.31 MPa | >= 480 psi | Stabilized, min | |
| 4.07 MPa | 590 psi | Stabilized, typ | |
| Compressive Modulus | 0.393 GPa | 57.0 ksi | Stabilized, typ |
| Shear Modulus | 0.0448 GPa | 6.50 ksi | Plate Shear, W Direction, typ |
| 0.0896 GPa | 13.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 0.896 MPa | >= 130 psi | Plate Shear, W Direction, min |
| 1.10 MPa | 160 psi | Plate Shear, W Direction, typ | |
| >= 1.45 MPa | >= 210 psi | Plate Shear, L Direction, min | |
| 2.14 MPa | 310 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |