- 缺口冲击强度: 5.87
- 拉伸强度 [MPa]: 255.0
- 弯曲模量 [MPa]: 25.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | |||
| Moisture Absorption at Equilibrium | 0.70 % @Thickness 1.57 mm | 0.70 % @Thickness 0.0620 in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 105 - 125 @Thickness 1.57 mm | 105 - 125 @Thickness 0.0620 in | |||
| Tensile Strength, Yield | 255 MPa @Thickness 3.17 mm | 37000 psi @Thickness 0.125 in | CW | ||
| 317 MPa @Thickness 3.17 mm | 46000 psi @Thickness 0.125 in | LW | |||
| Flexural Strength | 379 MPa @Thickness 1.57 mm | 55000 psi @Thickness 0.0620 in | CW | ||
| 441 MPa @Thickness 1.57 mm | 64000 psi @Thickness 0.0620 in | LW | |||
| Flexural Modulus | 25.5 GPa @Thickness 1.57 mm | 3700 ksi @Thickness 0.0620 in | CW | ||
| 27.6 GPa @Thickness 1.57 mm | 4000 ksi @Thickness 0.0620 in | LW | |||
| Compressive Strength | 455 MPa @Thickness 12.7 mm | 66000 psi @Thickness 0.500 in | Flatwise | ||
| Shear Strength | 172 MPa @Thickness 1.57 mm | 25000 psi @Thickness 0.0620 in | Perpendicular | ||
| Izod Impact, Notched | 5.87 J/cm @Thickness 12.7 mm | 11.0 ft-lb/in @Thickness 0.500 in | CW, E-48/50 | ||
| 6.94 J/cm @Thickness 12.7 mm | 13.0 ft-lb/in @Thickness 0.500 in | LW, E-48/50 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 300 °C | 572 °F | |||
| Decomposition Temperature | >= 385 °C | >= 725 °F | Degradation Temperature | ||
| Flammability, UL94 | HB | HB | |||
| Descriptive Properties | |||||
| Bond Strength | 1,600 lb | 0.5" | |||
| Conductivity Range Surface | 104ohm/Square | Preliminary | |||
| Glass Transition Temperature | None | ||||