- 拉伸强度 [MPa]: 63.4
- 弯曲模量 [MPa]: 10.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | >= 1.40 g/cc | >= 1.40 g/cc | |||
| Moisture Absorption at Equilibrium | 2.5 % @Thickness 1.57 mm | 2.5 % @Thickness 0.0620 in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 100 @Thickness 1.57 mm | 100 @Thickness 0.0620 in | |||
| Tensile Strength, Yield | 63.4 MPa @Thickness 3.17 mm | 9200 psi @Thickness 0.125 in | CW | ||
| 72.4 MPa @Thickness 3.17 mm | 10500 psi @Thickness 0.125 in | LW | |||
| Flexural Strength | 93.1 MPa @Thickness 1.57 mm | 13500 psi @Thickness 0.0620 in | CW | ||
| 93.1 MPa @Thickness 1.57 mm | 13500 psi @Thickness 0.0620 in | LW | |||
| Flexural Modulus | 10.3 GPa @Thickness 1.57 mm | 1500 ksi @Thickness 0.0620 in | CW | ||
| 10.3 GPa @Thickness 1.57 mm | 1500 ksi @Thickness 0.0620 in | LW | |||
| Compressive Strength | 172 MPa @Thickness 12.7 mm | 25000 psi @Thickness 0.500 in | Flatwise | ||
| Izod Impact, Unnotched | 0.294 J/cm @Thickness 12.7 mm | 0.550 ft-lb/in @Thickness 0.500 in | CW, E-48/50 | ||
| 0.320 J/cm @Thickness 12.7 mm | 0.600 ft-lb/in @Thickness 0.500 in | LW, E-48/50 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Breakdown | 5000 V @Thickness 1.57 mm | 5000 V @Thickness 0.0620 in | D-48/50 | ||
| 50000 V @Thickness 1.57 mm | 50000 V @Thickness 0.0620 in | Condition A | |||
| Arc Resistance | 120 sec @Thickness 3.17 mm | 120 sec @Thickness 0.125 in | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 10.0 µm/m-°C @Temperature 20.0 °C | 5.56 µin/in-°F @Temperature 68.0 °F | x-axis | ||
| CTE, linear, Transverse to Flow | 14.0 µm/m-°C @Temperature 20.0 °C | 7.78 µin/in-°F @Temperature 68.0 °F | y-axis | ||
| Maximum Service Temperature, Air | 120 °C | 248 °F | Maximum Operating Temperature | ||
| Flammability, UL94 | V-1 | V-1 | |||
| Descriptive Properties | |||||
| Bond Strength | 1,000 lb | 0.5" | |||