- 密度 [g/cm3]: 1.71
- 吸水率 [%]: 0.2
- 断裂伸长率 [%]: 76.0
- 弯曲强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ASTM D1895 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | Compression; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Compressive Yield Strength | 221 MPa | 32100 psi | ASTM D695 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.8 @Frequency 1e+6 Hz | 4.8 @Frequency 1e+6 Hz | ASTM D150 |
| 6.5 @Frequency 60 Hz | 6.5 @Frequency 60 Hz | ASTM D150 | |
| Dielectric Strength | 13.0 kV/mm | 330 kV/in | ASTM D149 |
| Dissipation Factor | 0.030 @Frequency 1e+6 Hz | 0.030 @Frequency 1e+6 Hz | ASTM D150 |
| 0.12 @Frequency 60 Hz | 0.12 @Frequency 60 Hz | ASTM D150 | |
| Comparative Tracking Index | 160 V | 160 V | UL 746 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| UL RTI, Mechanical with Impact | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| UL RTI, Mechanical without Impact | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| Flammability, UL94 | V-0 @Thickness 1.57 mm | V-0 @Thickness 0.0618 in | |
| V-0 @Thickness 1.57 mm | V-0 @Thickness 0.0618 in | ||