- 密度 [g/cm3]: 2.0
- 缺口冲击强度: 0.368
- 弯曲强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 16.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.00 g/cc | 0.0723 lb/in³ | ASTM D792A |
| Water Absorption | <= 0.10 % | <= 0.10 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D651 |
| Flexural Strength | 77.0 MPa | 11200 psi | ASTM D790 |
| Flexural Modulus | 16.0 GPa | 2320 ksi | ASTM D790 |
| Compressive Strength | 175 MPa | 25400 psi | ASTM D695 |
| Izod Impact, Notched | 0.368 J/cm | 0.689 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 9.10 kV/mm | 231 kV/in | Short Time; Dry; ASTM D149 |
| Arc Resistance | 190 sec | 190 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | |