- 密度 [g/cm3]: 2.1
- 弯曲模量 [MPa]: 12.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.900 - 1.05 g/cc | 0.0325 - 0.0379 lb/in³ | Powder Density; ISO 60 | ||
| Density | 2.10 g/cc | 0.0759 lb/in³ | Relative Density; ISO 1183 | ||
| Linear Mold Shrinkage | 0.0015 - 0.0025 cm/cm | 0.0015 - 0.0025 in/in | Injection Molding; ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 40.0 - 60.0 MPa | 5800 - 8700 psi | ISO 527 | ||
| Elongation at Break | 0.30 - 0.50 % | 0.30 - 0.50 % | Tensile; ISO 527 | ||
| 0.75 - 0.85 % | 0.75 - 0.85 % | Flexure; ISO 178 | |||
| Tensile Modulus | 17.5 - 19.5 GPa | 2540 - 2830 ksi | ISO 527 | ||
| Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | At Rupture; ISO 178 | ||
| Flexural Modulus | 12.0 - 14.0 GPa | 1740 - 2030 ksi | ISO 178 | ||
| Compressive Strength | 220 - 260 MPa | 31900 - 37700 psi | ISO 604 | ||
| Charpy Impact Unnotched | 0.400 - 0.600 J/cm² | 1.90 - 2.86 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.200 - 0.400 J/cm² | 0.952 - 1.90 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 243 | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 15.0 - 25.0 µm/m-°C @Temperature 20.0 °C | 8.33 - 13.9 µin/in-°F @Temperature 68.0 °F | TMA | ||
| CTE, linear, Transverse to Flow | 20.0 - 30.0 µm/m-°C @Temperature 20.0 °C | 11.1 - 16.7 µin/in-°F @Temperature 68.0 °F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 - 200 °C | 356 - 392 °F | ISO 75 Af | ||
| Deflection Temperature at 8.0 MPa | 155 - 170 °C | 311 - 338 °F | ISO 75 C | ||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |||
| V-0 @Thickness 4.00 mm | V-0 @Thickness 0.157 in | ||||
| Shrinkage | 0.050 - 0.15 % | 0.050 - 0.15 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| ISO type | PF 2 C3 | ||||
| Main Filler | Glass Fiber & Mineral | ||||
| Molding Method | Compression, transfer, injection | ||||