- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 Method A | ||
| Water Absorption | 0.60 % | 0.60 % | IPC TM-650 2.6.2.1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 44.8 MPa | 6500 psi | IPC TM-650 2.4.18.3 | ||
| Modulus of Elasticity | 15.9 GPa | 2300 ksi | IPC TM-650 2.4.18.3 | ||
| Flexural Strength | 234 MPa | 34000 psi | IPC TM-650 2.4.4 | ||
| Peel Strength | 0.684 kN/m | 3.90 pli | To Copper (1 oz./35 micron); After Process Solutions; IPC TM-650 2.4.8 | ||
| 0.754 kN/m | 4.30 pli | To Copper (1 oz./35 micron); After Thermal Stress; IPC TM-650 2.4.8 | |||
| 0.754 kN/m | 4.30 pli | To Copper (1 oz./35 micron); At Elevated Temperatures; IPC TM-650 2.4.8.2 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.40e+14 ohm-cm | 1.40e+14 ohm-cm | E24/125; IPC TM-650 2.5.17.1 | ||
| 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | C96/35/90; IPC TM-650 2.5.17.1 | |||
| Surface Resistance | 9.00e+13 ohm | 9.00e+13 ohm | E24/125; IPC TM-650 2.5.17.1 | ||
| 6.00e+14 ohm | 6.00e+14 ohm | C96/35/90; IPC TM-650 2.5.17.1 | |||
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | may vary with resin %; IPC TM-650 2.5.5.3 | ||
| Dielectric Strength | 39.4 kV/mm | 1000 kV/in | IPC TM-650 2.5.6.2 | ||
| Dissipation Factor | 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IPC TM-650 2.5.5.3 | ||
| Arc Resistance | 160 sec | 160 sec | IPC TM-650 2.5.1 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 6.00 - 9.00 µm/m-°C | 3.33 - 5.00 µin/in-°F | IPC TM-650 2.4.41 | ||
| CTE, linear, Transverse to Flow | 93.0 µm/m-°C | 51.7 µin/in-°F | z, below Tg; IPC TM-650 2.4.24 | ||
| 279 µm/m-°C | 155 µin/in-°F | z, above Tg; IPC TM-650 2.4.24 | |||
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM E1461 | ||
| Glass Transition Temp, Tg | 250 °C | 482 °F | TMA; IPC TM-650 2.4.24 | ||
| Decomposition Temperature | 393 °C | 739 °F | Initial; IPC TM-650 2.3.41 | ||
| 426 °C | 799 °F | 5 percent; IPC TM-650 2.3.41 | |||
| Descriptive Properties | |||||
| IPC Delamination - T260 (minutes) | >60 | IPC TM-650 2.4.24.1 | |||
| IPC Delamination - T288 (minutes) | >60 | IPC TM-650 2.4.24.1 | |||
| IPC Delamination - T300 (minutes) | >60 | IPC TM-650 2.4.24.1 | |||
| Z-Axis Expansion (%) | 2.3 | IPC TM-650 2.4.24 (50-260°C) | |||