- 密度 [g/cm3]: 0.9
- 拉伸强度 [MPa]: 0.965
- 弯曲强度 [MPa]: 0.016
- 脆化温度 [℃]: -60.0
- 透光率 [%]: 25.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 3.80 g/cc | 0.0325 - 0.137 lb/in³ | Average value: 1.85 g/cc Grade Count:231 |
| Oxygen Transmission | 88.0 - 150 cc-mm/m²-24hr-atm | 224 - 381 cc-mil/100 in²-24hr-atm | Average value: 104 cc-mm/m²-24hr-atm Grade Count:42 |
| Mooney Viscosity | 3.00 - 200 @Temperature 100 - 150 °C | 3.00 - 200 @Temperature 212 - 302 °F | Average value: 48.6 Grade Count:232 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 38.0 - 100 | 38.0 - 100 | Average value: 75.2 Grade Count:450 |
| 35.0 - 85.0 @Temperature 225 - 225 °C | 35.0 - 85.0 @Temperature 437 - 437 °F | Average value: 86.0 Grade Count:1 | |
| 58.0 - 98.0 @Temperature 93.3 - 200 °C | 58.0 - 98.0 @Temperature 200 - 392 °F | Average value: 86.0 Grade Count:11 | |
| 58.0 - 98.0 @Time 252000 - 3.60e+6 sec | 58.0 - 98.0 @Time 70.0 - 1000 hour | Average value: 86.0 Grade Count:11 | |
| Hardness, Shore D | 47.0 - 80.0 | 47.0 - 80.0 | Average value: 59.8 Grade Count:4 |
| Hardness, Shore M | 72.0 - 83.0 | 72.0 - 83.0 | Average value: 77.8 Grade Count:4 |
| Tensile Strength, Ultimate | 0.0160 - 27.0 MPa | 2.32 - 3920 psi | Average value: 13.7 MPa Grade Count:376 |
| 17.24 - 20.68 MPa @Temperature 225 - 225 °C | 2500 - 2999 psi @Temperature 437 - 437 °F | Average value: 17.8 MPa Grade Count:1 | |
| 8.40471 - 25.7933 MPa @Temperature 93.3 - 275 °C | 1219.00 - 3741.01 psi @Temperature 200 - 527 °F | Average value: 17.8 MPa Grade Count:16 | |
| 8.40471 - 25.7933 MPa @Time 86400 - 3.60e+6 sec | 1219.00 - 3741.01 psi @Time 24.0 - 1000 hour | Average value: 17.8 MPa Grade Count:16 | |
| Tensile Strength, Yield | 0.965 - 23.0 MPa | 140 - 3340 psi | Average value: 9.31 MPa Grade Count:143 |
| Elongation at Break | 28.0 - 500 % | 28.0 - 500 % | Average value: 194 % Grade Count:475 |
| 150 - 160 % @Temperature 225 - 225 °C | 150 - 160 % @Temperature 437 - 437 °F | Average value: 196 % Grade Count:1 | |
| 61.6 - 456.5 % @Temperature 93.3 - 275 °C | 61.6 - 456.5 % @Temperature 200 - 527 °F | Average value: 196 % Grade Count:16 | |
| 61.6 - 456.5 % @Time 86400 - 3.60e+6 sec | 61.6 - 456.5 % @Time 24.0 - 1000 hour | Average value: 196 % Grade Count:16 | |
| Modulus of Elasticity | 0.000600 - 0.140 GPa | 0.0870 - 20.3 ksi | Average value: 0.00736 GPa Grade Count:313 |
| Compressive Modulus | 0.000300 - 0.0153 GPa | 0.0435 - 2.22 ksi | Average value: 0.00534 GPa Grade Count:4 |
| Shear Modulus | 0.00193 - 0.0243 GPa | 0.280 - 3.53 ksi | Average value: 0.00760 GPa Grade Count:19 |
| 0.0430 - 0.0430 GPa @Temperature -12.0 - -12.0 °C | 6.24 - 6.24 ksi @Temperature 10.4 - 10.4 °F | Average value: 0.0430 GPa Grade Count:2 | |
| Secant Modulus | 0.00512 - 0.0685 GPa | 0.743 - 9.94 ksi | Average value: 0.0215 GPa Grade Count:19 |
| Coefficient of Friction | 0.500 - 1.16 | 0.500 - 1.16 | Average value: 0.791 Grade Count:51 |
| Tear Strength Test | 132 - 359 | 132 - 359 | Average value: 232 Grade Count:21 |
| Tear Strength | 3.06 - 31.4 kN/m | 17.5 - 179 pli | Average value: 21.5 kN/m Grade Count:87 |
| Taber Abrasion, mg/1000 Cycles | 40.0 - 325 | 40.0 - 325 | Average value: 184 Grade Count:5 |
| Compression Set | 5.00 - 69.0 % | 5.00 - 69.0 % | Average value: 26.1 % Grade Count:183 |
| 4.00 - 65.0 % @Temperature 100 - 300 °C | 4.00 - 65.0 % @Temperature 212 - 572 °F | Average value: 23.5 % Grade Count:265 | |
| 6.35 - 91.0 % @Temperature 93.3 - 316 °C | 6.35 - 91.0 % @Temperature 200 - 601 °F | Average value: 23.5 % Grade Count:74 | |
| 6.35 - 91.0 % @Time 79200 - 1.21e+6 sec | 6.35 - 91.0 % @Time 22.0 - 336 hour | Average value: 23.5 % Grade Count:74 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.00500 - 5.00e+17 ohm-cm | 0.00500 - 5.00e+17 ohm-cm | Average value: 4.06e+16 ohm-cm Grade Count:53 |
| Shielding Effectiveness | 70.0 - 113 dB | 70.0 - 113 dB | Average value: 98.3 dB Grade Count:3 |
| Dielectric Constant | 2.50 - 11.4 | 2.50 - 11.4 | Average value: 9.80 Grade Count:44 |
| Dielectric Strength | 2.60 - 25.0 kV/mm | 66.0 - 635 kV/in | Average value: 23.2 kV/mm Grade Count:50 |
| Dissipation Factor | 0.00500 | 0.00500 | Average value: 0.00500 Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 140 - 570 µm/m-°C | 77.8 - 317 µin/in-°F | Average value: 227 µm/m-°C Grade Count:48 |
| Specific Heat Capacity | 1.65 - 1.67 J/g-°C | 0.394 - 0.399 BTU/lb-°F | Average value: 1.65 J/g-°C Grade Count:40 |
| 0.945 - 1.053 J/g-°C @Temperature 50.0 - 150 °C | 0.226 - 0.2517 BTU/lb-°F @Temperature 122 - 302 °F | Average value: 0.991 J/g-°C Grade Count:4 | |
| Thermal Conductivity | 0.200 - 0.300 W/m-K | 1.39 - 2.08 BTU-in/hr-ft²-°F | Average value: 0.235 W/m-K Grade Count:40 |
| 0.170 - 0.190 W/m-K @Temperature 50.0 - 200 °C | 1.18 - 1.32 BTU-in/hr-ft²-°F @Temperature 122 - 392 °F | Average value: 0.180 W/m-K Grade Count:4 | |
| Maximum Service Temperature, Air | 93.3 - 350 °C | 200 - 662 °F | Average value: 232 °C Grade Count:280 |
| Minimum Service Temperature, Air | -65.0 - 0.000 °C | -85.0 - 32.0 °F | Average value: -19.7 °C Grade Count:253 |
| Brittleness Temperature | -60.0 - -6.00 °C | -76.0 - 21.2 °F | Average value: -23.4 °C Grade Count:91 |
| Glass Transition Temp, Tg | -51.1 - 3.00 °C | -60.0 - 37.4 °F | Average value: -16.6 °C Grade Count:125 |
| Transformation Temperature | -40.0 - -2.00 °C | -40.0 - 28.4 °F | Average value: -10.5 °C Grade Count:10 |
| Flash Point | 15.6 - 400 °C | 60.1 - 752 °F | Average value: 323 °C Grade Count:93 |
| Shrinkage | -21.0 - 25.0 % | -21.0 - 25.0 % | Average value: -3.60 % Grade Count:4 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 25.0 - 90.0 % | 25.0 - 90.0 % | Average value: 35.8 % Grade Count:6 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 - 170 °C | 320 - 338 °F | Average value: 165 °C Grade Count:25 |
| Cure Time | 1.50 - 4320 min | 0.0250 - 72.0 hour | Average value: 324 min Grade Count:27 |
| 10.0 - 10.0 min @Temperature 121 - 121 °C | 0.167 - 0.167 hour @Temperature 250 - 250 °F | Average value: 10.0 min Grade Count:2 | |
| Shelf Life | 12.0 - 240 Month | 12.0 - 240 Month | Average value: 188 Month Grade Count:19 |
| Component Elements Properties | Metric | English | Comments |
| Fluorine, F | 64.0 - 73.0 % | 64.0 - 73.0 % | Average value: 67.0 % Grade Count:52 |