- 弯曲强度 [MPa]: 3.34
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 3.70 g/cc | 3.70 g/cc | silicone property; Arlon SQA-TMS-024 | ||
| Thickness | 203 microns | 8.00 mil | overall; Arlon SQA-TMS-003 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 84 | 84 | silicone property; ASTM D2240 | ||
| Tensile Strength, Ultimate | 3.34 MPa | 485 psi | silicone property; ASTM D412 | ||
| Elongation at Break | 60 % | 60 % | silicone property; ASTM D412 | ||
| Modulus of Elasticity | 0.01957 GPa | 2.838 ksi | silicone property; Arlon SQA-TMS-008 | ||
| Poissons Ratio | 0.50 | 0.50 | silicone property | ||
| Shear Modulus | 0.372 GPa | 54.0 ksi | silicone property; ASTM D1002 | ||
| Shear Strength | 3.41 MPa | 495 psi | silicone property; ASTM D1002 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 0.050 ohm-cm | 0.050 ohm-cm | silicone property; ASTM D991 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 93.0 µm/m-°C @Temperature 20.0 °C | 51.7 µin/in-°F @Temperature 68.0 °F | silicone property; ASTM E 831 | ||
| Specific Heat Capacity | 0.400 J/g-°C | 0.0956 BTU/lb-°F | silicone property; ASTM E 1461-1 | ||
| Thermal Conductivity | 2.50 W/m-K | 17.4 BTU-in/hr-ft²-°F | silicone property; ASTM E 1530 | ||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -73.3 °C | -100 °F | |||
| Glass Transition Temp, Tg | -116 °C | -177 °F | silicone property; ASTM E 1356 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 141 °C | 0.250 hour @Temperature 285 °F | |||
| Shelf Life | 6.00 Month @Temperature 7.22 °C | 6.00 Month @Temperature 45.0 °F | |||
| Descriptive Properties | |||||
| Color | Naturally Gray | ||||