- 弯曲强度 [MPa]: 6.21
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | silicone property (alloy 600 = 8.41 g/cc); Arlon SQA-TMS-024 |
| Thickness | 25.4 microns | 1.00 mil | laminated foil; Arlon SQA-TMS-003 |
| 50.8 microns | 2.00 mil | side 1; Arlon SQA-TMS-003 | |
| 140 microns | 5.50 mil | side 2; Arlon SQA-TMS-003 | |
| 203 microns | 8.00 mil | substrate; Arlon SQA-TMS-003 | |
| 419 microns | 16.5 mil | overall; Arlon SQA-TMS-003 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 45 | 45 | silicone property; ASTM D2240 |
| Tensile Strength, Ultimate | 6.21 MPa | 900 psi | silicone property; ASTM D412 |
| Elongation at Break | 400 % | 400 % | silicone property; ASTM D412 |
| Adhesive Bond Strength | 0.0483 MPa | 7.00 psi | bond to alloy 600; ASTM D624 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 0.000103 ohm-cm | 0.000103 ohm-cm | alloy 600 property |
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 13.9 µm/m-°C @Temperature 20.0 °C | 7.72 µin/in-°F @Temperature 68.0 °F | alloy 600 property |
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | |
| Shelf Life | 12.0 Month @Temperature 21.1 °C | 12.0 Month @Temperature 70.0 °F | |