- 弯曲强度 [MPa]: 5.86
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | Arlon SQA-TMS-024 | ||
| Thickness | 127 microns | 5.00 mil | layer 1; Arlon SQA-TMS-003 | ||
| 152 microns | 6.00 mil | layer 2; Arlon SQA-TMS-003 | |||
| 432 microns | 17.0 mil | substrate; Arlon SQA-TMS-003 | |||
| 711 microns | 28.0 mil | overall; Arlon SQA-TMS-003 | |||
| Outgassing - Total Mass Loss | 0.34 % | 0.34 % | post cured; ASTM E 595 | ||
| 1.07 % | 1.07 % | no post cure; ASTM E 595 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 48 | 48 | silicone property; ASTM D2240 | ||
| Tensile Strength, Ultimate | 5.86 MPa | 850 psi | ASTM D412 | ||
| Elongation at Break | 450 % | 450 % | silicone property; ASTM D412 | ||
| Adhesive Bond Strength | 0.103 MPa | 15.0 psi | Arlon SQA-TMS-047 | ||
| Tear Strength | 12.3 kN/m | 70.0 pli | Die B; silicone property; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 14.4 kV/mm | 365 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 218 °C | 2.00 hour @Temperature 425 °F | |||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | ||||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||
| Outgassing - CVCM (%) ASTM E595 | 0.1 | post cured | |||
| 0.28 | no post cure | ||||