- 密度 [g/cm3]: 1.852
- 拉伸强度 [MPa]: 10.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.852 g/cc | 0.06691 lb/in³ | ASTM D3165 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 61 | 61 | ASTM D2240 | ||
| 59.41 @Treatment Temp. 200 °C, Time 252000 sec | 59.41 @Treatment Temp. 392 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Tensile Strength, Yield | 10.8 MPa | 1570 psi | ASTM D412 | ||
| 11.99 MPa @Treatment Temp. 200 °C, Time 252000 sec | 1739 psi @Treatment Temp. 392 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Elongation at Break | 273.2 % | 273.2 % | ASTM D412 | ||
| 191.24 % @Treatment Temp. 200 °C, Time 252000 sec | 191.24 % @Treatment Temp. 392 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Compressive Modulus | 0.000300 GPa @Strain 5.00 % | 0.0435 ksi @Strain 5.00 % | |||
| 0.000610 GPa @Strain 10.0 % | 0.0885 ksi @Strain 10.0 % | ||||
| 0.00122 GPa @Strain 20.0 % | 0.177 ksi @Strain 20.0 % | ||||
| 0.00171 GPa @Strain 25.0 % | 0.248 ksi @Strain 25.0 % | ||||
| Compression Set | 6.5 % @Temperature 175 °C, Time 79200 sec | 6.5 % @Temperature 347 °F, Time 22.0 hour | ASTM D395 | ||
| Descriptive Properties | |||||
| Color | Black | ||||