- 密度 [g/cm3]: 1.134
- 拉伸强度 [MPa]: 6.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.134 g/cc | 0.04097 lb/in³ | ASTM D3165 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 32 | 32 | ASTM D2240 | ||
| 30.4 @Treatment Temp. 200 °C, Time 252000 sec | 30.4 @Treatment Temp. 392 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Tensile Strength, Yield | 6.50 MPa | 943 psi | ASTM D412 | ||
| 3.8155 MPa @Treatment Temp. 200 °C, Time 252000 sec | 553.39 psi @Treatment Temp. 392 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Elongation at Break | 709.2 % | 709.2 % | ASTM D412 | ||
| 539.7 % @Treatment Temp. 200 °C, Time 252000 sec | 539.7 % @Treatment Temp. 392 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Compressive Modulus | 0.000200 GPa @Strain 5.00 % | 0.0290 ksi @Strain 5.00 % | |||
| 0.000320 GPa @Strain 10.0 % | 0.0464 ksi @Strain 10.0 % | ||||
| 0.000410 GPa @Strain 20.0 % | 0.0595 ksi @Strain 20.0 % | ||||
| 0.000750 GPa @Strain 25.0 % | 0.109 ksi @Strain 25.0 % | ||||
| Compression Set | 6.31 % @Temperature 175 °C, Time 79200 sec | 6.31 % @Temperature 347 °F, Time 22.0 hour | ASTM D395 | ||
| Descriptive Properties | |||||
| Color | Cool Gray | ||||