- 弯曲强度 [MPa]: 12.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 | ||
| Brookfield Viscosity | 50 cP @Temperature 23.9 °C | 50 cP @Temperature 75.0 °F | Part B; ASTM D2393 | ||
| 3600 cP @Temperature 23.9 °C | 3600 cP @Temperature 75.0 °F | initial mixed; ASTM D2393 | |||
| 6000 cP @Temperature 23.9 °C | 6000 cP @Temperature 75.0 °F | Part A; ASTM D2393 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 82 - 85 | 82 - 85 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 12.1 MPa | 1750 psi | ASTM D412 | ||
| Elongation at Break | 720 % | 720 % | ASTM D412 | ||
| Tensile Modulus | 0.00379 GPa | 0.550 ksi | 1; ASTM D412 | ||
| Tear Strength | 30.7 kN/m | 175 pli | ASTM 4-624-54 Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 960 - 1440 min @Temperature 24.0 °C | 16.0 - 24.0 hour @Temperature 75.2 °F | demold time | ||
| 4320 - 7200 min @Temperature 24.0 °C | 72.0 - 120 hour @Temperature 75.2 °F | full cure | |||
| Pot Life | 25 min @Temperature 24.0 °C | 25 min @Temperature 75.2 °F | gel time; ASTM D2471 | ||
| Descriptive Properties | |||||
| Mix Ratio | 4:1 by weight (A/B) | ||||