- 弯曲强度 [MPa]: 0.5
- 透光率 [%]: 90.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 35 | 35 | |||
| Tensile Strength, Ultimate | 0.5000 MPa | 72.52 psi | |||
| Elongation at Break | 60 % | 60 % | |||
| Modulus of Elasticity | 0.0011000 GPa | 0.15954 ksi | at 150% elongation, maximum | ||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.396 | 1.396 | |||
| 1.404 | 1.404 | ||||
| 1.394 @Wavelength 1554 nm | 1.394 @Wavelength 1554 nm | ||||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 150 °C | 1.00 hour @Temperature 302 °F | |||
| Shelf Life | 6.00 Month | 6.00 Month | |||
| Descriptive Properties | |||||
| Mix Ratio (X:1) | 100 | Base to Catalyst ETN | |||