- 弯曲强度 [MPa]: 15.2
- 脆化温度 [℃]: -24.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 68 | 68 | |||
| Tensile Strength, Ultimate | 15.2 MPa | 2200 psi | |||
| Elongation at Break | 280 % | 280 % | |||
| 100% Modulus | 0.00510 GPa | 0.740 ksi | |||
| Compression Set | 6.0 % | 6.0 % | 70 hrs at 150°C, method B, plied | ||
| 12 % | 12 % | 168 hrs at 150°C, method B, plied | |||
| 24 % | 24 % | 168 hrs at 177°C, method B, plied | |||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | <= -24.0 °C | <= -11.2 °F | TR-10 | ||
| Clash Berg Stiffness Temperature | -26.0 °C | -14.8 °F | At 69 MPa | ||
| Descriptive Properties | |||||
| Armeen® 18D | 0.5 parts | ||||
| DIAK No. 7(TIAC) | 1.5 parts | ||||
| DOTG Coaccelerator | 4 parts | ||||
| Naugard® 445 antioxidant | 1 part | ||||
| SRF Black(N774) | 65 parts | ||||
| Stearic Acid | 1.5 parts | ||||
| Vamac® G | 100 parts | ||||
| Vanfre® VAM | 1 part | ||||