- 弯曲强度 [MPa]: 16.4
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Mooney Viscosity | 55 @Temperature 100 °C | 55 @Temperature 212 °F | ML(1+4); ASTM D1646 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 64 | 64 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 16.4 MPa | 2380 psi | ASTM D412 | ||
| Elongation at Break | 275 % | 275 % | ASTM D412 | ||
| 100% Modulus | 0.00600 GPa | 0.870 ksi | ASTM D412 | ||
| Compression Set | 16 % | 16 % | 70 hrs at 150°C; ASTM D395 | ||
| Descriptive Properties | |||||
| Armeen® 18D | 0.5 phr | ||||
| Diak No. 1 | 1.5 phr | ||||
| DOTG Coaccelerator | 4 phr | ||||
| Mooney Scorch at 121°C, Minimum Viscosity | 23.4 metric minutes | Mooney Units, ASTM D1646 | |||
| Mooney Scorch at 121°C, t10 | 10.5 metric minutes | Time for 10 unit rise, ASTM D1646 | |||
| Mooney Scorch at 121°C, t18 | 17.6 metric minutes | Time for 18 unit rise, ASTM D1646 | |||
| N550 Black | 60 phr | ||||
| Naugard® 445 antioxidant | 2 phr | ||||
| Stearic Acid | 1.5 phr | ||||
| TP-761 | 10 phr | ||||
| Vamac® HVG | 100 phr | ||||
| Vanfre® VAM | 1.5 phr | ||||