- 弯曲强度 [MPa]: 16.2
- 脆化温度 [℃]: -17.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 83 | 83 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D2240-91 |
| Tensile Strength, Ultimate | 16.2 MPa | 2350 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| Elongation at Break | 125 % | 125 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| 100% Modulus | 0.0131 GPa | 1.90 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| Tear Strength | 27.1 kN/m | 155 pli | Die C, Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 24 % @Temperature 200 °C | 24 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414-94 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -17.0 °C | 1.40 °F | Temperature Retraction, TR-10, using 50% elongation; ASTM D1329-88 |