- 弯曲强度 [MPa]: 14.8
- 脆化温度 [℃]: -19.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 71 | 71 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D2240-91 |
| Tensile Strength, Ultimate | 14.8 MPa | 2150 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| Elongation at Break | 205 % | 205 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| 100% Modulus | 0.00680 GPa | 0.986 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| Tear Strength | 21.9 kN/m | 125 pli | Die C, Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 14 % @Temperature 200 °C | 14 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414-94 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -19.0 °C | -2.20 °F | Temperature Retraction, TR-10; ASTM D1329-88 |