- 弯曲强度 [MPa]: 11.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Elongation at Break | 275 % | 275 % | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| 100% Modulus | 0.00480 GPa | 0.696 ksi | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Compression Set | 31 % @Temperature 200 °C | 31 % @Temperature 392 °F | Method B, O-rings, 70 hr |