- 弯曲强度 [MPa]: 19.6
- 脆化温度 [℃]: -27.7
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Tensile Strength, Ultimate | 19.6 MPa | 2840 psi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Elongation at Break | 222 % | 222 % | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Modulus of Elasticity | 0.000710 GPa | 0.103 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| 100% Modulus | 0.00690 GPa | 1.00 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -27.7 °C | -17.9 °F | TR-10, 100% Elongation |
| Glass Transition Temp, Tg | -27.3 °C | -17.1 °F | DSC |