- 弯曲强度 [MPa]: 19.6
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 19.6 MPa | 2840 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 289 % | 289 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.000700 GPa | 0.102 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00420 GPa | 0.609 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 11 % @Temperature 200 °C | 11 % @Temperature 392 °F | Method B, O-rings 22 hr at 200°C (Post Cured 4 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | -18.8 °C | -1.84 °F | MDSC, postcured |