- 密度 [g/cm3]: 1.057
- 弯曲强度 [MPa]: 13.5
- 脆化温度 [℃]: -45.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.057 g/cc | 0.03819 lb/in³ | |
| Mooney Viscosity | 33 @Temperature 100 °C | 33 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 58 | 58 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 13.5 MPa | 1960 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 685 % | 685 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00160 GPa | 0.232 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00270 GPa | 0.392 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00380 GPa | 0.551 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 29.5 kN/m | 168 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 95 % @Temperature 125 °C | 95 % @Temperature 257 °F | Pellets cured MDR TC95 + 15 min at 160°C, 70 hr at 125°C; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -45.0 °C | -49.0 °F | Temperature Retraction, TR-10 |