- 密度 [g/cm3]: 1.09
- 弯曲强度 [MPa]: 9.5
- 脆化温度 [℃]: -44.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | |
| Mooney Viscosity | 27 @Temperature 100 °C | 27 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 64 | 64 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 9.50 MPa | 1380 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 360 % | 360 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00300 GPa | 0.435 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00790 GPa | 1.15 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 27.9 kN/m | 159 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 74 % @Temperature 125 °C | 74 % @Temperature 257 °F | Pellets cured MDR TC95 + 15 min at 160°C, 70 hr at 125°C; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -44.0 °C | -47.2 °F | Temperature Retraction, TR-10 |