- 密度 [g/cm3]: 1.055
- 弯曲强度 [MPa]: 18.9
- 脆化温度 [℃]: -47.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.055 g/cc | 0.03811 lb/in³ | |
| Mooney Viscosity | 122 @Temperature 100 °C | 122 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 64 | 64 | Vulcanizate, Press cured, TC95 +3min at 180°C |
| Tensile Strength, Ultimate | 18.9 MPa | 2740 psi | Vulcanizate, Press cured, TC95 +3min at 180°C |
| Elongation at Break | 255 % | 255 % | Vulcanizate, Press cured, TC95 +3min at 180°C |
| 50% Modulus | 0.00190 GPa | 0.276 ksi | Vulcanizate, Press cured, TC95 +3min at 180°C |
| 100% Modulus | 0.00400 GPa | 0.580 ksi | Vulcanizate, Press cured, TC95 +3min at 180°C |
| 200% Modulus | 0.0126 GPa | 1.83 ksi | Vulcanizate, Press cured, TC95 +3min at 180°C |
| Tear Strength | 22.1 kN/m | 126 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 180°C |
| Compression Set | 3.0 % @Temperature 100 °C | 3.0 % @Temperature 212 °F | Pellets cured MDR TC95 + 15 min at 160°C, 22 hr at 100°C; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -47.0 °C | -52.6 °F | Temperature Retraction, TR-10 |