- 弯曲强度 [MPa]: 19.0
- 脆化温度 [℃]: -34.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 44 @Temperature 100 °C | 44 @Temperature 212 °F | ML 1+4. Stock property.; ASTM D1646-81 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 67 | 67 | ASTM D2240-81 |
| Tensile Strength, Ultimate | 19.0 MPa | 2760 psi | ASTM D412-80 |
| Elongation at Break | 550 % | 550 % | ASTM D412-80 |
| 100% Modulus | 0.00600 GPa | 0.870 ksi | ASTM D412-80 |
| Resilience | 58 | 58 | % Yerzley; ASTM D945-77 |
| Tear Strength Test | 328 | 328 | lb-in. Graves Die C; ASTM D642-54 |
| Abrasion | 146 | 146 | NBS Abrasion Index; ASTM D1630-74. |
| Compression Set | 59 % @Temperature 70.0 °C | 59 % @Temperature 158 °F | 22 hr at 70°C. Method B. ASTM D395-69 |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -34.0 °C | -29.2 °F | Brittleness Temperature |
| Brittleness Temperature | -34.0 °C | -29.2 °F | ASTM D746-79 |
| Clash Berg Stiffness Temperature | -21.0 °C | -5.80 °F | T-10000 Torsional stiffness ASTM D1043-72(1981) |