- 密度 [g/cm3]: 1.8
- 弯曲强度 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | |
| Oxygen Transmission | 98.0 cc-mm/m²-24hr-atm | 249 cc-mil/100 in²-24hr-atm | |
| Mooney Viscosity | 23 @Temperature 121 °C | 23 @Temperature 250 °F | ML1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 79 | 79 | |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | |
| Elongation at Break | 180 % | 180 % | |
| Modulus of Elasticity | 0.00730 GPa | 1.06 ksi | M100 |
| Coefficient of Friction, Dynamic | 0.80 | 0.80 | |
| Compression Set | 13 % @Temperature 200 °C | 13 % @Temperature 392 °F | 70 hr; ASTM D395B |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 1.00e+14 ohm-cm | 1.00e+13 - 1.00e+14 ohm-cm | |
| Dielectric Constant | 11.4 @Frequency 6.00e+7 Hz | 11.4 @Frequency 6.00e+7 Hz | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 200 µm/m-°C @Temperature 20.0 °C | 111 µin/in-°F @Temperature 68.0 °F | |
| Specific Heat Capacity | 1.65 J/g-°C | 0.394 BTU/lb-°F | |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | |
| Glass Transition Temp, Tg | -18.0 °C | -0.400 °F | TR10 |