- 密度 [g/cm3]: 1.55
- 弯曲强度 [MPa]: 20.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | |
| Oxygen Transmission | 150 cc-mm/m²-24hr-atm | 381 cc-mil/100 in²-24hr-atm | |
| Mooney Viscosity | 160 @Temperature 100 °C | 160 @Temperature 212 °F | ML1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 71 | 71 | |
| Tensile Strength, Ultimate | 20.0 MPa | 2900 psi | |
| Elongation at Break | 330 % | 330 % | |
| Modulus of Elasticity | 0.00330 GPa | 0.479 ksi | M100 |
| Coefficient of Friction, Dynamic | 0.70 | 0.70 | |
| Compression Set | 44 % @Temperature 200 °C | 44 % @Temperature 392 °F | 70 hr; ASTM D395B |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 - 1.00e+16 ohm-cm | 1.00e+15 - 1.00e+16 ohm-cm | |
| Dielectric Constant | 2.5 @Frequency 6.00e+7 Hz | 2.5 @Frequency 6.00e+7 Hz | |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 240 µm/m-°C @Temperature 20.0 °C | 133 µin/in-°F @Temperature 68.0 °F | |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | |
| Glass Transition Temp, Tg | 3.00 °C | 37.4 °F | TR10 |