Physical PropertiesMetricEnglishComments
Specific Gravity 1.80 g/cc1.80 g/cc
Mooney Viscosity 17
@Temperature 100 °C
17
@Temperature 212 °F
ML1+10
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore A 7777Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C; ASTM D2240
Tensile Strength at Break 13.9 MPa2010 psiPress Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
Elongation at Break 170 %170 %Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C; ASTM D4645
100% Modulus 0.00448 GPa0.650 ksiPress Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
Compression Set 19 %19 %Aged 70 hours @ 200°C, -214 O-rings; ASTM D395 Method B
 
Thermal PropertiesMetricEnglishComments
Transformation Temperature -18.0 °C-0.400 °FTR10; ASTM D1329
 
Component Elements PropertiesMetricEnglishComments
Fluorine, F 65.9 %65.9 %
 
Descriptive Properties
ColorOpaque Off-White
MH, Maximum Torque 16.6 inch-lb 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289
ML, Minimum Torque0.3 inch-lb100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289
SolubilityKetones and Esters
t`50, Time to 50% cure1.7 minutes100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289
t`90 - Time to 90% cure2.7 minutes100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289
ts2 - Time to n-lb rise from min1.5 minutes100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-36587.html

免责声明: 本文 3M Dyneon™ FC 2110Q Fluoroelastomer 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4