- 密度 [g/cm3]: 0.4
- 吸水率 [%]: 0.3
- 拉伸强度 [MPa]: 0.586
- 弯曲强度 [MPa]: 11.0
- 热变形温度 [℃]: 67.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.400 - 1.20 g/cc | 0.0145 - 0.0434 lb/in³ | Average value: 0.969 g/cc Grade Count:7 |
| Water Absorption | 0.300 - 4.00 % | 0.300 - 4.00 % | Average value: 2.24 % Grade Count:7 |
| Water Absorption at Saturation | 0.300 - 4.00 % | 0.300 - 4.00 % | Average value: 2.24 % Grade Count:7 |
| Viscosity | 50.0 - 3600 cP @Temperature 82.2 - 82.2 °C | 50.0 - 3600 cP @Temperature 180 - 180 °F | Average value: 385 cP Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 1.00 - 95.0 | 1.00 - 95.0 | Average value: 77.4 Grade Count:11 |
| Hardness, Shore D | 50.0 - 60.0 | 50.0 - 60.0 | Average value: 56.0 Grade Count:3 |
| Tensile Strength, Ultimate | 11.0 - 50.0 MPa | 1600 - 7250 psi | Average value: 31.4 MPa Grade Count:7 |
| Tensile Strength, Yield | 0.586 - 42.7 MPa | 85.0 - 6200 psi | Average value: 28.3 MPa Grade Count:12 |
| Elongation at Break | 4.00 - 900 % | 4.00 - 900 % | Average value: 413 % Grade Count:18 |
| Modulus of Elasticity | 0.440 - 2.00 GPa | 63.8 - 290 ksi | Average value: 1.08 GPa Grade Count:7 |
| Rebound | 5.00 - 70.0 % | 5.00 - 70.0 % | Average value: 41.2 % Grade Count:9 |
| Charpy Impact Unnotched | 0.900 J/cm² - NB | 4.28 ft-lb/in² - NB | Average value: 3.52 J/cm² Grade Count:7 |
| 0.772 - 0.772 J/cm² @Temperature -30.0 - -30.0 °C | 3.67 - 3.67 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 0.772 J/cm² Grade Count:1 | |
| Tear Strength | 23.5 - 83.3 kN/m | 134 - 475 pli | Average value: 50.8 kN/m Grade Count:11 |
| Taber Abrasion, mg/1000 Cycles | 3.00 - 85.0 | 3.00 - 85.0 | Average value: 31.8 Grade Count:10 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 7.00e+13 - 1.00e+15 ohm-cm | 7.00e+13 - 1.00e+15 ohm-cm | Average value: 4.88e+14 ohm-cm Grade Count:6 |
| Surface Resistance | 1.00e+13 - 2.00e+14 ohm | 1.00e+13 - 2.00e+14 ohm | Average value: 5.67e+13 ohm Grade Count:6 |
| Dielectric Strength | 10.0 - 18.0 kV/mm | 254 - 457 kV/in | Average value: 14.7 kV/mm Grade Count:6 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 54.0 - 160 µm/m-°C | 30.0 - 88.9 µin/in-°F | Average value: 105 µm/m-°C Grade Count:7 |
| CTE, linear, Transverse to Flow | 73.0 - 164 µm/m-°C | 40.6 - 91.1 µin/in-°F | Average value: 120 µm/m-°C Grade Count:7 |
| Maximum Service Temperature, Air | 82.2 °C | 180 °F | Average value: 82.2 °C Grade Count:11 |
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 - 195 °C | 153 - 383 °F | Average value: 142 °C Grade Count:5 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 - 136 °C | 131 - 277 °F | Average value: 97.5 °C Grade Count:4 |
| Vicat Softening Point | 94.0 - 245 °C | 201 - 473 °F | Average value: 163 °C Grade Count:4 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 22.2 - 82.2 °C | 72.0 - 180 °F | Average value: 76.8 °C Grade Count:11 |
| Mold Temperature | 22.2 - 82.2 °C | 72.0 - 180 °F | Average value: 76.8 °C Grade Count:11 |
| Cure Time | 25.0 - 360 min | 0.417 - 6.00 hour | Average value: 59.5 min Grade Count:11 |
| Pot Life | 2.50 - 15.0 min | 2.50 - 15.0 min | Average value: 3.97 min Grade Count:10 |