- 密度 [g/cm3]: 0.58
- 断裂伸长率 [%]: 37.0
- 弯曲强度 [MPa]: 17.0
- 弯曲模量 [MPa]: 1.42
- 热变形温度 [℃]: 49.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.580 g/cc | 0.0210 lb/in³ | ASTM D792 |
Apparent Bulk Density | 0.580 g/cc | 0.0210 lb/in³ | ASTM D792 |
Linear Mold Shrinkage | 0.0024 cm/cm | 0.0024 in/in | Bayer Test |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 43 | 43 | ASTM D2240 |
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638/D412 |
Elongation at Break | 11 % | 11 % | ASTM D638/D412 |
Flexural Yield Strength | 37.0 MPa | 5370 psi | ASTM D790 |
Flexural Modulus | 1.42 GPa | 206 ksi | ASTM D790 |
Izod Impact, Unnotched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
Thermal Properties | Metric | English | Comments |
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |