- 密度 [g/cm3]: 1.04
- 缺口冲击强度: 4.8
- 弯曲强度 [MPa]: 23.0
- 弯曲模量 [MPa]: 0.320
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 51 | 51 | ASTM D2240 |
| Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | ASTM D638/D412 |
| Elongation at Break | 360 % | 360 % | ASTM D638/D412 |
| Flexural Modulus | 0.320 GPa | 46.4 ksi | ASTM D790 |
| Izod Impact, Notched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D256 |
| Tear Strength | 87.0 kN/m | 496 pli | Die C; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 153 µm/m-°C @Temperature 20.0 °C | 85.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Flammability, UL94 | V-2 @Thickness 3.18 mm | V-2 @Thickness 0.125 in | |
| V-2 @Thickness 3.18 mm | V-2 @Thickness 0.125 in | ||