- 密度 [g/cm3]: 1.05
- 吸水率 [%]: 2.0
- 弯曲强度 [MPa]: 50.0
- 热变形温度 [℃]: 115.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Water Absorption | 2.0 % | 2.0 % | Saturation in water |
| Water Absorption at Saturation | 2.0 % | 2.0 % | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | |
| Elongation at Break | 12 % | 12 % | |
| Tensile Modulus | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 µm/m-°C @Temperature 20.0 °C | 50.0 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 20.0 °C | 50.0 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | |
| Vicat Softening Point | 135 °C | 275 °F | |
| Flammability, UL94 | V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | |