Mechanical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Peel Strength | 0.438 kN/m | 2.50 pli | To Aluminum, Ambient Temperature; ASTM D1000 | ||
0.438 kN/m | 2.50 pli | To Steel, Ambient Temperature; ASTM D1000 | |||
0.525 kN/m @Treatment Temp. 177 °C, Time 173000 sec | 3.00 pli @Treatment Temp. 351 °F, Time 48.0 hour | To Steel; ASTM D1000 | |||
0.5425 kN/m @Treatment Temp. 177 °C, Time 173000 sec | 3.096 pli @Treatment Temp. 351 °F, Time 48.0 hour | To Aluminum; ASTM D1000 | |||
0.6825 kN/m @Treatment Temp. 177 °C, Time 3600 sec | 3.894 pli @Treatment Temp. 351 °F, Time 1.00 hour | To Steel; ASTM D1000 | |||
0.700 kN/m @Treatment Temp. 177 °C, Time 3600 sec | 3.99 pli @Treatment Temp. 351 °F, Time 1.00 hour | To Aluminum; ASTM D1000 | |||
0.700 kN/m @Treatment Temp. 74.0 °C, Time 173000 sec | 3.99 pli @Treatment Temp. 165 °F, Time 48.0 hour | 95% RH, To Steel; ASTM D1000 | |||
0.7175 kN/m @Treatment Temp. 74.0 °C, Time 173000 sec | 4.094 pli @Treatment Temp. 165 °F, Time 48.0 hour | 95% RH, To Aluminum; ASTM D1000 | |||
0.875 kN/m @Treatment Temp. 204 °C, Time 3600 sec | 4.99 pli @Treatment Temp. 399 °F, Time 1.00 hour | To Steel; ASTM D1000 | |||
0.8925 kN/m @Treatment Temp. 204 °C, Time 3600 sec | 5.093 pli @Treatment Temp. 399 °F, Time 1.00 hour | To Aluminum; ASTM D1000 | |||
Compression Set | <= 20 % | <= 20 % | 25% Deflection; ASTM D395 Method B | ||
Electrical Properties | Metric | English | Comments | ||
Surface Resistivity per Square | 0.0070 ohm @Temperature 121 °C, Time 605000 sec | 0.0070 ohm @Temperature 250 °F, Time 168 hour | Initial; CHO-TM-TP57 | ||
0.0070 ohm @Temperature 35.0 °C, Time 605000 sec | 0.0070 ohm @Temperature 95.0 °F, Time 168 hour | 95% RH, Initial; CHO-TM-TP57 | |||
0.0090 ohm @Temperature 85.0 °C, Time 605000 sec | 0.0090 ohm @Temperature 185 °F, Time 168 hour | Initial; CHO-TM-TP57 | |||
0.010 ohm @Temperature 35.0 °C, Time 605000 sec | 0.010 ohm @Temperature 95.0 °F, Time 168 hour | 95% RH, Final; CHO-TM-TP57 | |||
0.010 ohm @Temperature 70.0 °C, Time 7.88e+6 sec | 0.010 ohm @Temperature 158 °F, Time 2190 hour | Initial; CHO-TM-TP57 | |||
0.010 ohm @Temperature 70.0 °C, Time 7.88e+6 sec | 0.010 ohm @Temperature 158 °F, Time 2190 hour | Final; CHO-TM-TP57 | |||
0.014 ohm @Temperature 85.0 °C, Time 605000 sec | 0.014 ohm @Temperature 185 °F, Time 168 hour | Final; CHO-TM-TP57 | |||
0.017 ohm @Temperature 121 °C, Time 605000 sec | 0.017 ohm @Temperature 250 °F, Time 168 hour | Final; CHO-TM-TP57 | |||
Shielding Effectiveness | 80 dB @Frequency 1.00e+10 Hz | 80 dB @Frequency 1.00e+10 Hz | CHO-TM-TP08 | ||
90 dB @Frequency 1.00e+8 Hz | 90 dB @Frequency 1.00e+8 Hz | CHO-TM-TP08 | |||
93 dB @Frequency 1.00e+9 Hz | 93 dB @Frequency 1.00e+9 Hz | CHO-TM-TP08 | |||
Thermal Properties | Metric | English | Comments | ||
Maximum Service Temperature, Air | 70.0 °C | 158 °F | |||
Flammability, UL94 | HB | HB | |||
Descriptive Properties | |||||
Adhesion | >2.5 lb/in | Initial PSA, ASTM D1000 | |||
Compression Cycling | 10000 cycles at 50% Deflection, Final | ||||
10000 cycles at 50% Deflection, Initial | |||||
Compression-Deflection, 25% deflection | <3 to <9 psi | ASTM D3574 Modified | |||
Core | PORON Urethane Foam | ||||
Jacket | Fabric-Reinforced Aluminum Foil | ||||
PSA Type | Chomerics Electrically Conductive Acrylic |