- 密度 [g/cm3]: 1.01
- 吸水率 [%]: 0.2
- 弯曲强度 [MPa]: 13.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | |||
| Water Absorption | 0.20 % | 0.20 % | 24 hours | ||
| Water Absorption at Saturation | 0.0040 % | 0.0040 % | 30 Days | ||
| Viscosity | 6800 cP @Temperature 25.0 °C | 6800 cP @Temperature 77.0 °F | |||
| Linear Mold Shrinkage | 0.0115 cm/cm | 0.0115 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 90 | 90 | Tolerance of +/- 5 | ||
| Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | |||
| Elongation at Break | 450 % | 450 % | |||
| Tear Strength | 48.2 kN/m | 275 pli | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 4.30e+15 ohm-cm | <= 4.30e+15 ohm-cm | |||
| Insulation Resistance | >= 2.50e+13 ohm | >= 2.50e+13 ohm | Value at 25°C | ||
| Dielectric Constant | 2.8 @Frequency 1e+6 Hz | 2.8 @Frequency 1e+6 Hz | |||
| 3.0 @Frequency 100 Hz | 3.0 @Frequency 100 Hz | ||||
| Dielectric Strength | 29.5 kV/mm @Thickness 1.59 mm, Temperature 25.0 °C | 750 kV/in @Thickness 0.0625 in, Temperature 77.0 °F | |||
| Dissipation Factor | 0.012 @Frequency 1e+6 Hz | 0.012 @Frequency 1e+6 Hz | |||
| 0.032 @Frequency 100 Hz | 0.032 @Frequency 100 Hz | ||||
| Arc Resistance | >= 120 sec | >= 120 sec | Value at 25°C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 240 - 360 min | 4.00 - 6.00 hour | 80°C | ||
| 10080 min | 168.0 hour | 25°C | |||
| Pot Life | 70 min | 70 min | Value for 0.5 lbm at 25°C | ||
| Descriptive Properties | |||||
| Color | Opaque Amber | ||||