- 密度 [g/cm3]: 1.22
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0442 lb/in³ | |||
| Viscosity | 10000 cP | 10000 cP | Mixed Viscosity | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 83 | 83 | Cured; ASTM D2240 | ||
| Tensile Strength at Break | 17.9 MPa | 2600 psi | ASTM D412 | ||
| Elongation at Break | <= 800 % | <= 800 % | ASTM D412 | ||
| Tear Strength | 57.0 kN/m | 325 pli | ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 11.8 kV/mm | 300 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 48.9 °C | 120 °F | wet | ||
| 82.2 °C | 180 °F | dry | |||
| Shrinkage | 0.14 % | 0.14 % | Cured; ASTM D2566 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min | 2.00 hour | Functional cure | ||
| Pot Life | 10 min | 10 min | at 75°F | ||
| Descriptive Properties | |||||
| Coverage per pound, in² @ 1/4" thickness | 90 | ||||
| Mix ratio by weight (Resin:Hardener) | 63:37 | ||||