- 密度 [g/cm3]: 0.899
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.899 g/cc | 0.0325 lb/in³ | ASTM D1475 | ||
| Solids Content | 50 % | 50 % | Fed Std 141 Method 4044 | ||
| Volatile Organic Compounds (VOC) Content | <= 225 g/l | <= 225 g/l | |||
| Viscosity | 200 cP | 200 cP | Fed Std Method 4287 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Modulus of Elasticity | 0.02699 GPa | 3.915 ksi | |||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | 1.60e+10 ohm | 1.60e+10 ohm | Moisture Resistance; MIL-I-46058C | ||
| Insulation Resistance | 2.00e+14 ohm | 2.00e+14 ohm | Insulation Resistance; MIL-I-46058C | ||
| Dielectric Constant | 3.6 | 3.6 | ASTM D1 50 65T | ||
| Dielectric Breakdown | >= 1500 V | >= 1500 V | Dielectric Withstand; MIL-I-46058C | ||
| Dissipation Factor | 0.020 | 0.020 | ASTM D1 50 65T | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 170 µm/m-°C @Temperature 20.0 °C | 94.4 µin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 125 °C | 257 °F | |||
| Minimum Service Temperature, Air | -65.0 °C | -85.0 °F | |||
| Glass Transition Temp, Tg | 56.0 °C | 133 °F | |||
| Flash Point | 15.6 °C | 60.0 °F | ASTM D56 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 20.0 min | 0.333 hour | Dry Time to Handling; Fed Std 141 4061 | ||
| 1200 min | 20.0 hour | 190°C | |||
| 1800 min | 30.0 hour | 170°C | |||
| 10800 - 43200 min | 180 - 720 hour | at room temp optimum properties in 7 - 30 days. | |||
| Shelf Life | 12.0 Month | 12.0 Month | Shelf life listed at room temperature; store below 80°F | ||
| Descriptive Properties | |||||
| Coverage | 375 ft²/gal | ||||