- 密度 [g/cm3]: 1.11
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.11 g/cc | 0.0400 lb/in³ | |||
| Viscosity | 12000 cP | 12000 cP | Mixed Viscosity | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 94 | 94 | Cured; ASTM D2240 | ||
| Tensile Strength at Break | 22.8 MPa | 3300 psi | ASTM D412 | ||
| Elongation at Break | <= 350 % | <= 350 % | ASTM D412 | ||
| Tear Strength | 90.3 kN/m | 515 pli | ASTM D624 | ||
| Taber Abrasion, mg/1000 Cycles | 88 | 88 | H-18 wheel (1000 gram load) | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 13.8 kV/mm | 350 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 121 °C | 250 °F | wet | ||
| 177 °C | 350 °F | dry | |||
| Shrinkage | 0.14 % | 0.14 % | Cured; ASTM D2566 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min | 1.00 hour | Functional cure | ||
| Pot Life | 3.0 min | 3.0 min | at 75°F | ||
| Descriptive Properties | |||||
| Coverage per pound, in² @ 1/4" thickness | 100 | ||||
| Mix ratio by weight (Resin:Hardener) | 80:20 | ||||