- 密度 [g/cm3]: 1.09
- 拉伸强度 [MPa]: 27.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D1475 | ||
| Solids Content | 37.2 % | 37.2 % | by volume; ASTM D2369 Modified | ||
| 49.5 % | 49.5 % | by weight; ASTM D2369 Modified | |||
| Volatile Organic Compounds (VOC) Content | 550 g/l | 550 g/l | ASTM D3960 | ||
| Brookfield Viscosity | 450 cP | 450 cP | ASTM D2196, LVT, Spindle #2 @ 30rpm | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | Coatings catalyzed 2% with 9995, baked 15 minutes @ 107ºC, post cured 2 weeks @ 25ºC and 50% relative humidity. Free films tested on an Instron tester | ||
| Elongation at Yield | 250 % | 250 % | Coatings catalyzed 2% with 9995, baked 15 minutes @ 107ºC, post cured 2 weeks @ 25ºC and 50% relative humidity. Free films tested on an Instron tester | ||
| Thermal Properties | Metric | English | Comments | ||
| Flash Point | 20.0 °C | 68.0 °F | ASTM D3278, Seta Flash, Closed Cup | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 1.00 - 4.00 min @Temperature 149 - 191 °C | 0.0167 - 0.0667 hour @Temperature 300 - 376 °F | |||
| 2.00 - 5.00 min @Temperature 121 - 149 °C | 0.0333 - 0.0833 hour @Temperature 250 - 300 °F | ||||
| 10.0 - 30.0 min @Temperature 93.0 - 121 °C | 0.167 - 0.500 hour @Temperature 199 - 250 °F | ||||
| Descriptive Properties | |||||
| Appearance | White | ||||
| Theoretical Coverage (ft²/gallon/mil) | 595 | ||||