- 拉伸强度 [MPa]: 70.3
- 弯曲模量 [MPa]: 2.51
- 热变形温度 [℃]: 58.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc @Temperature 23.9 °C | 1.08 g/cc @Temperature 75.0 °F | |
| Viscosity | 2000 cP @Temperature 23.9 °C | 2000 cP @Temperature 75.0 °F | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 45 - 48 | 45 - 48 | clear casting |
| Tensile Strength, Yield | 70.3 MPa | 10200 psi | Clear Casting |
| Tensile Modulus | 2.67 GPa | 387 ksi | clear casting |
| Flexural Strength | 87.6 MPa | 12700 psi | clear casting |
| Flexural Modulus | 2.51 GPa | 364 ksi | clear casting |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 58.0 °C | 136 °F | clear casting; unspecified load |
| Processing Properties | Metric | English | Comments |
| Gel Time | 40.0 - 60.0 min @Temperature 23.9 °C | 40.0 - 60.0 min @Temperature 75.0 °F | when reacted at 1:1.3 by weight, based on the application |
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | Sealed containers should be stored between 75ºF and 95ºF |