- 拉伸强度 [MPa]: 16.45
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 65 | 65 | |
| Tensile Strength, Yield | 16.45 MPa | 2386 psi | |
| Elongation at Yield | 551 % | 551 % | |
| 100% Modulus | 0.00294 GPa | 0.427 ksi | |
| 200% Modulus | 0.00598 GPa | 0.867 ksi | |
| 300% Modulus | 0.009970 GPa | 1.446 ksi | |
| Tear Strength | 53.6 kN/m | 306 pli | |
| Taber Abrasion, mg/1000 Cycles | 8.0 @Load 1.00 kg | 8.0 @Load 2.20 lb | H-18 wheel |
| Compression Set | 53.8 % @Temperature 70.0 °C, Time 79200 sec | 53.8 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 11.0 min @Temperature 154 °C | 0.183 hour @Temperature 309 °F | |