- 拉伸强度 [MPa]: 18.62
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | |
| Tensile Strength, Yield | 18.62 MPa | 2701 psi | |
| Elongation at Yield | 668 % | 668 % | |
| 100% Modulus | 0.00188 GPa | 0.272 ksi | |
| 200% Modulus | 0.00270 GPa | 0.391 ksi | |
| 300% Modulus | 0.00369 GPa | 0.535 ksi | |
| Tear Strength | 41.2 kN/m | 235 pli | |
| Taber Abrasion, mg/1000 Cycles | 32 @Load 1.00 kg | 32 @Load 2.20 lb | H-18 wheel |
| Compression Set | 77.6 % @Temperature 70.0 °C, Time 79200 sec | 77.6 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 11.0 min @Temperature 154 °C | 0.183 hour @Temperature 309 °F | |