- 拉伸强度 [MPa]: 34.5
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 68 | 68 | |||
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | |||
| Elongation at Break | 560 % | 560 % | |||
| 300% Modulus | 0.0138 GPa | 2.00 ksi | |||
| Tear Strength | 66.4 kN/m | 379 pli | Die C; ASTM D624 | ||
| Abrasion | 355 | 355 | NBS Index | ||
| Compression Set | 24 % @Temperature 70.0 °C, Time 79200 sec | 24 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 142 °C | 1.00 hour @Temperature 287 °F | |||
| Descriptive Properties | |||||
| Mooney Scorch | >30 | time to 10 point rise (minutes) at 250ºF | |||
| 20 | time to 10 point rise (minutes) at 275ºF | ||||