- 拉伸强度 [MPa]: 16.5
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 81 | 81 | |||
| Tensile Strength, Yield | 16.5 MPa | 2400 psi | |||
| Elongation at Yield | 464 % | 464 % | |||
| 100% Modulus | 0.00400 GPa | 0.580 ksi | |||
| 200% Modulus | 0.008170 GPa | 1.185 ksi | |||
| 300% Modulus | 0.01218 GPa | 1.767 ksi | |||
| Tear Strength | 41.0 kN/m | 234 pli | Die C | ||
| Compression Set | 68 % @Temperature 70.0 °C, Time 79200 sec | 68 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 34.0 min @Temperature 160 °C | 0.567 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm³) | 107 | ||||