- 拉伸强度 [MPa]: 19.5
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore A | 90 | 90 | |
Tensile Strength, Yield | 19.5 MPa | 2830 psi | |
Elongation at Yield | 226 % | 226 % | |
100% Modulus | 0.01474 GPa | 2.138 ksi | |
200% Modulus | 0.01925 GPa | 2.792 ksi | |
Tear Strength | 53.4 kN/m | 305 pli | Die C |
Taber Abrasion, mg/1000 Cycles | 0.26 | 0.26 | H-18, mg loss/rev |
Compression Set | 62 % @Temperature 70.0 °C, Time 79200 sec | 62 % @Temperature 158 °F, Time 22.0 hour | |
Processing Properties | Metric | English | Comments |
Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F |