- 拉伸强度 [MPa]: 25.39
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 80 | >= 80 | |||
| Tensile Strength, Yield | 25.39 MPa | 3683 psi | |||
| Elongation at Yield | 431 % | 431 % | |||
| 100% Modulus | 0.00689 GPa | 1.00 ksi | |||
| 200% Modulus | 0.01420 GPa | 2.059 ksi | |||
| 300% Modulus | 0.01939 GPa | 2.813 ksi | |||
| Tear Strength | 39.4 kN/m | 225 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm³) | 48 | ||||