- 拉伸强度 [MPa]: 28.59
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 58 | >= 58 | |||
| Tensile Strength, Yield | 28.59 MPa | 4147 psi | |||
| Elongation at Yield | 626 % | 626 % | |||
| 100% Modulus | 0.00280 GPa | 0.406 ksi | |||
| 200% Modulus | 0.00620 GPa | 0.899 ksi | |||
| 300% Modulus | 0.009301 GPa | 1.349 ksi | |||
| Tear Strength | 40.6 kN/m | 232 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 16.0 min @Temperature 68.3 °C | 0.267 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm³) | 80.5 | ||||